Bis(phenolic-amine)quinone compounds and polyolefin compositions stabilized therewith

ABSTRACT

Disclosed is a class of bis(phenolic-amine)quinone compounds which are useful as stablizers for polyolefins. The bis(phenolic-amine)quinone compounds inhibit oxidative degradation of polyolefins which is attributable to heat and/or ultraviolet light and is promoted or accelerated by metals, e.g., copper, in contact with the polyolefin. The compounds also exhibit excellent thermal stability.

This invention pertains to certain novel bis(phenolic amine)quinone compounds which are useful as metal deactivators and antioxidants in polyolefins. This invention also pertains to polyolefin compositions containing one or more of the bis(phenolic amine)quinone compounds.

Poly-α-olefins require the presence therein of stabilizers to prevent or retard oxidative, thermal and/or ultraviolet light deterioration. The most common of such poly-α-olefins are low, medium and high density polymers derived from ethylene, propylene, mixtures thereof and copolymers of ethylene and minor amounts of higher α-olefins such as 1- butene, 1 -hexene, 1 -octene, 1-dodecene, etc. Stabilizers typically present in such poly-α-olefins include a phenolic antioxidant such as 2,2-bis[[3-[3,5-bis(2-methyl-2-propyl)-4-hydroxyphenyl]-1-oxopropoxy]methyl]-1,3-propanediyl 3,5-bis(1,1-dimethylethyl)-4-hydroxybenzenepropanoate (Irganox 1010 stabilizer) or 2,6-bis(1-methylheptadecyl)-p-cresol, phosphites such as trihydrocarbyl phosphites including cyclic phosphites and sulfides such as thiodipropionate esters such as dilauryl thiodipropionate.

When poly-α-olefin compositions are used as coatings for metals, e.g., as wire coating compositions, the compositions also contain a metal deactivator to inhibit polymer degradation which is promoted or accelerated by the metal. For example, polyolefin compositions used to coat copper wire typically contain a copper deactivator such as N,N'-dibenzaloxalyldihydrazide. For some wire coating applications, it is necessary that the metal deactivator resist leaching from the polyolefin when it is in contact with such materials as petrolatum used as a filler in electrical cables. However, most commercial phenolic antioxidants such as Irganox 1010 are readily leached from the polyolefin coating by petrolatum.

One embodiment of the present invention pertains to a class of novel bis(phenolic-amine)quinone compounds which function as both phenolic antioxidants and metal deactivators when incorporated into poly-α-olefins intended for use in coating metal articles, particularly copper wire. These novel compounds have the general formula: ##STR1## wherein X is alkylene or cycloalkylene; and

Y is a tertiary hydrocarbyl group having the formula ##STR2## wherein Z is alkyl or aryl. The alkylene groups which X may represent contain up to about 12 carbon. The cycloalkylene groups represented by X may contain from 4 to 7 ring carbon atoms. X preferably is alkylene of 2 to 8 carbon atoms. Examples of the alkyl groups represented by Z include alkyl containing up to about 8 carbon such as methyl, ethyl, propyl, 2-propyl, butyl, 2-butyl, 2-methyl 2-propyl, pentyl, 2-pentyl, hexyl, 2-ethyl hexyl, 2,4,4-trimethyl-2-pentyl. The alkyl groups preferably contain up to 4 carbon atoms. The aryl group represented by Z may be unsubstituted phenyl or phenyl substituted with 1 or 2 groups selected from lower, i.e., containing up to about 4 carbon atoms, alkyl, lower alkoxy or halogen, e.g., chlorine or bromine. Z most preferably is methyl, i.e., the hydrocarbyl group represented by Y is 2-methyl-2-propyl (tertiary butyl).

A second embodiment of the invention pertains to a polyolefin composition comprising an intimate mixture of (i) a normally-solid polymer of ethylene, propylene, a mixture of ethylene and propylene or polymers of ethylene and an α-olefin having 4 to 12 carbon atoms and (ii) 1 or more compounds of formula (I) above. The concentration of the compound of formula (I) which will effectively inhibit polymer degradation can vary considerably depending on the particular polymer being stabilized and the end use for which the stabilized polymeric material is designed. Generally, concentrations the range of 0.05 to 5.0 weight percent may be used with concentrations of about 0.1 to 1.0 being most common. The stabilizers provided by this invention may be used in combination with other conventional stabilizers such as polyvalent salts of organic acids, thioethers, phosphites and ultraviolet light stabilizers. In addition, other additives, such as plasticizers, lubricants, emulsifiers, antistatic agents, flame retardant agents, pigments and fillers, commonly used in formulating commercial polymeric compositions may be present.

The novel stabilizer compounds provided by the present invention may be prepared in accordance with conventional synthesis procedures by reacting a phenolic-amide-amine having the structure: ##STR3## with para-benzoquinone at elevated temperatures in the presence of an inert solvent such as an alkanol. The intermediates of formula (II) may be prepared from alkyl 3-arylpropionate esters and various diamines.

The preparation and use of the stabilizers of the invention are further illustrated by the following examples.

EXAMPLE 1

A solution of N-(2-aminoethyl)-3-[3,5-bis(2-methyl-2-propyl)-4-hydroxyphenyl]propionamide (0.0875 mol) in ethanol (100 mL) at 50° C. is added slowly over a period of 30 minutes p-benzoquinone (0.132 mol) in ethanol (120 mL). The mixture is heated to and maintained at reflux temperature for 6 hours. The mixture then is cooled to room temperature and the product is collected by filtration, washed with acetone and dried. The product is obtained in a yield of 60% and has a melting point of 262-265° C. and the structure: ##STR4##

EXAMPLE 2

A solution of N-(6-aminohexyl)-3-[3,5-bis(2-methyl-2-propyl)-4-hydroxyphenyl]propionamide (0.0875 mol) in ethanol (100 mL) at 50° C. is added slowly over a period of 30 minutes p-benzoquinone (0.132 mol) in ethanol (120 mL). The mixture is heated to and maintained at reflux temperature for 6 hours. The mixture then is cooled to room temperature and the product is collected by filtration, washed with acetone and dried. The product is obtained in a yield of 60% and has a melting point of 80-110° C. and the structure: ##STR5##

The polyolefin compositions provided by the present invention may be prepared by incorporating one or more of the bis(phenolic-amine)quinones described hereinabove into poly-α-olefin polymers by conventional blending techniques. For example, the bis(phenolic-amine)quinone compounds may be added directly to a melt of the polyolefin on a roll mill to distribute the bis(phenolic-amine)quinone compound uniformly throughout the polymer. Alternatively, the compounds may be dry-blended with a finely-divided form of the polyolefin such as pellets and then the dry mix can be mixed further in and extruded from an extruder.

The novel polyolefin compositions of the invention are particularly useful for coating copper materials such as copper wires. Thus, a third embodiment of the present invention pertains to a coated article comprising a copper material, especially copper wire, bearing a coating of one of the polyolefin compositions described herein.

EXAMPLE 3 AND COMPARATIVE EXAMPLE 1

The bis(phenolic-amine)quinone compound prepared as described in Example 1 is evaluated as a stabilizer in and for polyethylene according to the following procedure. The amounts of materials employed are given in parts by weight. The compound of Example 1 (1.2 parts) is dry mixed with a sample (600 parts) of unstabilized, high density polyethylene (Alathon 7050, Oxy Chemical). The mixture then is fed to and extruded from a C. W. Brabender conical, twin-screw extruder at 200° C. over a period of 2 minutes. The extruded polyolefin composition is pelletized and the pellets are pressed into film 254 microns thick at a temperature of 200° C. and a pressure of 68.95 megapascals (10,000 pounds per square inch) using a Carver laboratory press. Film also is prepared from the same high density polyethylene which did not contain any bis(phenolic-amine)quinone compound.

The stability of the film samples of the polyolefin compositions is determined by Differential Scanning Calorimetry (DSC) analysis according to the general procedure described by Ellerstein, "The Use of Dynamic Differential Calorimetry for Ascertaining the Thermal Stability of Polymers," Analytical Calorimetry, Eds., R. S. Porter and J. F. Johnson, Plenum, New York, 1968, p. 279 and by Wright, "Oxidative Stability of Expanded Polyethylene for Wire and Cable," J. Cell. Plast., 6, 317 (1976). A 3-4 mg sample of each film is placed in an aluminum or copper pan without the lid and scanned at a rate of 20° C. per minute from 40 to 300° C. under forced air at a rate of 15 mL per minute. Degradation of a polyolefin composition occurs at the temperature at which an oxidative exotherm is observed. The thermal oxidative degradation of polyolefins is essentially a controlled burning and thus produces heat which is detected by the DSC instrument. A stabilizer which increases the temperature at which degradation begins increases the overall usefulness of the polyolefin. The onset temperature of the oxidative exotherm curve that is measured as the degradation temperature of a sample is determined as the intercept of the baseline before degradation starts and the following straight line when degradation occurs.

The temperature at which each polyolefin composition grades, determined as described above, is shown in Table I. Degradation temperatures are given in Table I for the film samples scanned in the aluminum pan and the copper pan. It is apparent from the examples of Table I, including Comparative Example 1 (C-1), that the copper of the copper pan promotes or accelerates the degradation of the film samples of the polyolefin compositions. It also is apparent that the presence of one of the bis(phenolic-amine)quinone compounds of the present invention in the polyethylene improves the stability thereof by raising the temperature at which the polyolefin composition degrades, as determined in both the aluminum (Al) pan and in the copper (Cu) pan.

                  TABLE I                                                          ______________________________________                                                      Degradation Temperature, °C.                               Example        Al Pan     Cu Pan                                               ______________________________________                                         C-1            239        220                                                  1              261        260                                                  ______________________________________                                    

The thermal stability of the bis(phenolic-amine)-quinone compounds prepared as described in Examples 1 and 2 is determined by thermogravimetric analysis and compared with the thermal stability of a known phenolichydrazide metal deactivator, N,N'-bis[3-[3,5-bis(2-methyl-2-propyl)-4-hydroxyphenyl]propionyl]hydrazide (MD-1024). A sample of each compound was placed in a thermobalance and heated at a rate of 20° C. per minute from 25° C. to 600° C. The heating was performed in both air and in a nitrogen atmosphere. The weight loss of each sample is recorded as a function of temperature.

The temperatures at which the samples have lost 5 weight percent of their weight are:

    ______________________________________                                         Compound of Example 1:                                                                             325° C. in nitrogen                                                     315° C. in air                                      Compound of Example 2:                                                                             325° C. in nitrogen                                                     305° C. in air                                      MD-1024:            290° C. in nitrogen                                                     290° C. in air                                      ______________________________________                                    

The above data show that the thermal stability of the bis(phenolic-amine)quinone compounds of the present invention is superior to that of the known phenolichydrazide compound MD-1024.

The invention has been described in detail with particular reference to preferred embodiments thereof, but it will be understood that variations and modifications may be effected within the spirit and scope of the invention. 

We claim:
 1. A compound having the formula: ##STR6## wherein X is alkylene or cycloalkylene; andY is a tertiary hydrocarbyl group having the formula ##STR7## wherein Z is alkyl or aryl.
 2. A compound according to claim 1 having the formula ##STR8##
 3. A compound according to claim 1 having the formula ##STR9##
 4. A polyolefin composition comprising an intimate mixture of(i) a normally solid polymer of ethylene, propylene, a mixture of ethylene and propylene or polymers of ethylene and an α-olefin having 4 to 12 carbon atoms; and (ii) a compound having the formula: ##STR10## wherein X is alkylene or cycloalkylene; andY is a tertiary hydrocarbyl group having the formula ##STR11## wherein Z is alkyl or aryl.
 5. A composition according to claim 4 wherein component (i) is polyethylene and the concentration of component (ii) is about 0.1 to 1.0 weight percent based on the total weight of the composition.
 6. A composition according to claim 4 wherein component (ii) is a compound having the formula: ##STR12##
 7. A composition according to claim 4 wherein component (ii) is a compound having the formula: ##STR13##
 8. A coated article comprising a copper material bearing a coating of a polyolefin composition comprising(i) a normally solid polymer of ethylene, propylene, a mixture of ethylene and propylene or polymers of ethylene and an α-olefin having 4 to 12 carbon atoms; and (ii) a compound having the formula: ##STR14## wherein X is alkylene or cycloalkylene; andY is a tertiary hydrocarbyl group having the formula ##STR15## wherein Z is alkyl or aryl. 